Fracture zone Characterization – Micro-Mechanical Study (1)
Publication Name: Wood and fiber science
Publication URL: https://wfs.swst.org/index.php/wfs/article/view/137/137
The experimental and numerical characterization of the fracture process zone in softwoods is pre-
scented. In-situ real-time Scanning Electron Microscopy (SEM) was used as a tool to examine the physical mechanism of fracture in softwoods (spruce)using end-tapered Double Cantilever Beam
specimens. The fracture process zone has been characterized in terms of failure mechanisms. It was found that bridging behind the crack tip is the main toughening mechanism, which contributes to nonlinear wood behavior in the presence of stress concentrations.