Fracture Zone Characterization Micro-mechanical Study (2)

Published: 2002

Author(s):

Vasic, Svetlana
Smith, I.
Landis, Eric

Publication Name: Wood and Fiber Science

Publication URL: https://wfs.swst.org/index.php/wfs/article/view/137

Research Area:

Wood Composites

Keywords:

Nanocellulose

Abstract:

The experimental and numerical characterization of the fracture process zone in softwoods is presented. In-situ real-time Scanning Electron Microscopy (SEM) was used as a tool to examine the physical mechanism of fracture in softwoods (spruce) using end-tapered Double Cantilever Beam specimens. Fracture process zone has been characterized in terms of failure mechanisms. It was found that bridging behind the crack tip is the main toughening mechanism, which contributes to nonlinear wood behavior in the presence of stress concentrations.