Surface Preparation and Treatment for Large-Scale 3D-Printed Composite Tooling Coating Adhesion

Published: 2018

Author(s):
Sauerbier, P.
Anderson, J.
Gardner, D.J.

Publication Name: Coatings

Publication URL: https://www.mdpi.com/2079-6412/8/12/457/htm

Research Area:
Keywords:
, ,

Abstract:

Recent advances in large-scale thermoplastic additive manufacturing (AM), using fused deposition modelling (FDM), have shown that the technology can effectively produce large aerospace tools with common feed stocks, costing 2.3 $/kg, such as a 20% carbon-filled acrylonitrile butadiene styrene (ABS). Large-scale additive manufacturing machines have build-volumes in the range of cubic meters and use commercially available pellet feedstock thermoplastics, which are significantly cheaper (5–10 $/kg) than the filament feedstocks for desktop 3D printers (20–50 $/kg). Additionally, large-scale AM machines have a higher material throughput on the order of 50 kg/h. This enables the cost-efficient tool production for several industries. Large-scale 3D-printed tooling will be computerized numerical control (CNC)-machined and -coated, to provide a surface suitable for demolding the composite parts. This paper outlines research undertaken to review and improve the adhesion of the coating systems to large, low-cost AM composite tooling, for marine or infrastructure composite applications. Lower cost tooling systems typically have a lower dimensional accuracy and thermal operating requirements than might be required for aerospace tooling. As such, they can use lower cost commodity grade thermoplastics. The polymer systems explored in the study included polypropylene (PP), styrene-maleic anhydride (SMA), and polylactic acid (PLA). Bio-based filler materials were used to reduce cost and increase the strength and stiffness of the material. Fillers used in the study included wood flour, at 30% by weight and spray-dried cellulose nano-fibrils, at 20% by weight. Applicable adhesion of the coating was achieved with PP, after surface treatment, and untreated SMA and PLA showed desirable coating adhesion results. PLA wood-filled composites offered the best properties for the desired application and, furthermore, they have environment-friendly advantages.