Melt compounding of spray-dried cellulose nanofibrils/polypropylene and their application in 3D printing
Published: 2024
Publication Name: Cellulose
Publication URL: https://doi.org/10.1007/s10570-024-06038-w
Abstract:
Micro- and nano-scale cellulosic fillers exhibit excellent dispersion and distribution within a thermoplastic matrix during the process of melt compounding or injection molding. In this study, spray-dried cellulose nanofiber (SDCNF) powders were manufactured using a pilot-scale rotating disk atomizer spray dryer. Bleached Kraft pulp (BKP), unbleached Kraft pulp (UKP), and old corrugated cardboard pulp (OCC) fibrillated at a fines level of 90% were used as feedstock materials for spray-drying. BKP-, UKP-, and OCC- SDCNFs were compounded with polypropylene using a twin screw co-rotating extruder. Maleic anhydride grafted polypropylene (MAPP) was used as a coupling agent in the composite formulations. The tensile, flexural, and impact properties of SDCNF-filled PP composites increased at 10 wt% SDCNF loading. The presence of SDCNFs in the PP matrix resulted in faster crystallization and a 12% reduction in the degree of crystallinity of the neat PP. The coefficient of thermal expansion (CTE) of neat PP was reduced by up to 31% attributable to the presence of the SDCNFs. Application of the SDCNF-reinforced PP composites in 3D printing reduced the shrinkage rate of the printed neat PP by 39%, and the printability of the PP was significantly improved with the addition of the SDCNFs.