Impact properties and rheological behavior of exfoliated GraphiteNanoplatelet-Filled Impact Modified Polypropylene Nanocomposites

Published: 2014

Author(s):

Duguay, A.
Kiziltas, A.
Nader, J.
Gardner D. J.
Dagher, H.

Publication Name: Journal of Nanoparticle Research 16

Publication URL: https://link.springer.com/article/10.1007/s11051-014-2307-4

Research Area:

Smart Materials & Textiles, Thermoplastics

Keywords:

exfoliated graphite nanoplatelets (xGnP), Nanocellulose

Abstract:

Exfoliated graphite nanoplatelets (xGnP)-filled impact modified polypropylene (IMPP) composites were prepared at 2, 4, 6, and 8 wt% xGnP with and without the addition of a coupling agent and manufactured using melt mixing followed by injection molding. The coupling agent used in this study was polypropylene-graft-maleic anhydride. The nanoparticles used were xGnP with three different sizes: xGnP5 has an average thickness of 10 nm, and an average platelet diameter of 5 ?m, whereas xGnP15 and xGnP25 have the same thickness but average diameters are 15 and 25 ?m, respectively. Test results show that nanocomposites with smaller xGnP diameter exhibited better impact properties for both neat and compatibilized composites. However, unnotched and notched impact strengths as well as fracture initiation resistance were dramatically deteriorated with the introduction of xGnP. Explanation of this brittle behavior in a nanoplatelet-filled IMPP is presented using melt flow index and transmission electron microscopy.